Title | : | Effect of Sulfation on Physicochemical Properties of ZrO2 and TiO2 Nanoparticles |
Author | : |
Prof. Dr. rer. nat. Karna Wijaya, M.Eng. (1) REMI AYU PRATIKA (2) Wahyu Dita Saputri (7) Dr. Dra. Sri Mulijani, MSi (8) Aep Patah, S.Si., M.Si., Ph.D. (9) Arief Cahyo Wibowo (10) |
Date | : | 7 2022 |
Keyword | : | sulphated,zirconia,titania,acidity,calcination sulphated,zirconia,titania,acidity,calcination |
Abstract | : | Effect of sulfation processes on the physicochemical properties of ZrO2 and TiO2 nanoparticles were thoroughly investigated. SO4/ZrO2 and SO4/TiO2 catalysts were synthesized to identify the acidity character of each. The wet impregnation method of ZrO2 and TiO2 nanoparticles was employed using H2SO4 with various concentrations of 0.5, 0.75, and 1 M, followed by calcination at 400, 500, and 600 °C to obtain optimum conditions of the catalyst synthesis process. The highest total acidity was found when using 1 M SO4/ZrO2-500 and 1 M SO4/TiO2-500 catalysts, with total acidity values of 2.642 and 6.920 mmol/g, respectively. Sulfation increases titania particles via agglomeration. In contrast, sulfation did not practically change the size of zirconia particles. The sulfation process causes color of both catalyst particles to brighten due to the presence of sulfate. There was a decrease in surface area and pore volume of catalysts after sulfation; the materials’ mesoporous structural properties were confirmed. The 1 M SO4/ZrO2 and 1 M SO4/TiO2 catalysts calcined at 500 °C are the best candidate heterogeneous acid catalysts synthesized in thus work. |
Group of Knowledge | : | Kimia |
Original Language | : | English |
Level | : | Internasional |
Status | : |
Published
|
No | Title | Action |
---|---|---|
1 |
KJMR -Article_compressed.pdf
Document Type : Bukti Published
|
View |
2 |
Artikel KJMR-similarity.pdf
Document Type : [PAK] Cek Similarity
|
View |
3 |
KJMR -Article_compressed.pdf
Document Type : [PAK] Full Dokumen
|
View |
4 |
(3) form-L1-permohonan_penghargaan-karya-ilmiah-sudah-terbit-2022_Karna Wijaya.pdf
Document Type : Dokumen Pendukung Karya Ilmiah (Hibah, Publikasi, Penelitian, Pengabdian)
|
View |
5 |
Universitas Gadjah Mada Mail - ??????-??????.pdf
Document Type : [PAK] Bukti Korespondensi Penulis
|
View |