Title | : | Performance of Ni-Mo Sulfated Nanozirconia Catalyst for Conversion of Waste Cooking Oil Into Biofuel via Hydrocracking Process |
Author | : |
ARNIZ HANIFA (1) ASMA NADIA (2) WAHYU DITA SAPUTRI (3) Akhmad Syoufian, Ph.D. (4) Prof. Dr. rer. nat. Karna Wijaya, M.Eng. (5) |
Date | : | 6 2021 |
Keyword | : | NiMO-SZ; ,sulfated zirconia,hydrocracking,conversion,cooking oil NiMO-SZ; ,sulfated zirconia,hydrocracking,conversion,cooking oil |
Abstract | : | The synthesis of the Ni-Mo sulfated zirconia (NiMo-SZ) catalyst and its application to convert waste cooking oil into biofuel was successfully conducted. The synthesis process was started with a sulfation process on the zirconia oxide (ZrO2) using 0.5, 1.0, and 1.5 M sulfuric acid (H2SO4) through wet impregnation to obtain sulfated zirconia (SZ). Solid SZ with the highest total acidity value was calcined at temperature 500, 550, 600, 650, and 700 °C. Solid SZ calcined with the optimum temperature was treated with Ni and Mo metals at 1%, 2%, and 3% (w/w) through a hydrothermal method. Pure ZrO2, SZ, and 1, 2, and 3 NiMo-SZ catalysts were used in the hydrocracking of used cooking oil into biofuel. The results showed that the 1.5 M SZ catalyst calcined at 500 °C had the highest acidity value of 3.8137 mmol/g. The 3-NiMo-SZ catalyst had the best activity valuing at 80.54%, while 1-NiMo-SZ produced the best selectivity in producing gasoline fraction until 73.93%. |
Group of Knowledge | : | Kimia |
Original Language | : | English |
Level | : | Internasional |
Status | : |
Published
|
No | Title | Action |
---|---|---|
1 |
form-L1-permohonan_penghargaan-karya-ilmiah-sudah-terbit-2021.pdf
Document Type : Dokumen Pendukung Karya Ilmiah (Hibah, Publikasi, Penelitian, Pengabdian)
|
View |
2 |
Jurnal Material Science Forum.pdf
Document Type : Dokumen Pendukung Karya Ilmiah (Hibah, Publikasi, Penelitian, Pengabdian)
|
View |
3 |
paperarniz-turnitin.pdf
Document Type : [PAK] Cek Similarity
|
View |
4 |
MSF_1045_79.pdf
Document Type : [PAK] Full Dokumen
|
View |
5 |
Universitas Gadjah Mada Mail - Materials Science Forum.pdf
Document Type : [PAK] Bukti Korespondensi Penulis
|
View |