Title : Preparation and characterization of montmorillonite-cetyl trimethylammonium bromide
Author :

Sri Hilma Siregar (1) Prof. Dr. rer. nat. Karna Wijaya, M.Eng. (2) Prof. Eko Sri Kunarti, M.Si., Ph.D. (3) Akhmad Syoufian, Ph.D. (4) Dr. Suyanta, M.Si. (5)

Date : 30 2017
Keyword : Montmorillonite,Organo-montmorillonite,Surfactant cationic Montmorillonite,Organo-montmorillonite,Surfactant cationic
Abstract : The research was focused on the modification of natural montmorillonite by using cationic surfactant cetyl trimethylammonium bromide (CTAB). The natural bentonite was washed with distilled water to clean the impurites of nature bentonite in order to get the montmorillonite fraction. A variation of the amount of CTAB, which is used for the preparation of organo-montmorillonite is 0.5; 1.0; 1.5; 2.0; 2.5 CEC of montmorillonite. The organically intercalated montmorillonite composites were characterized by FT-IR, XRD, Brunauer-Emmett-Teller (BET) surface area techniques and SEM-EDX-Mapping methods. The effect of addition of CTAB on the basal spacing of montmorillonite was observed with XRD, indicating an increase in basal spacing (d001) of montmorillonite 14.671 (2? = 6.02) to 19.153 Å (4.61°). The main bands of untreated montmorillonite at 3626 cm–1 attributed to stretching vibration of structural hydroxyl groups (-OH) and 1041 cm–1 assigned to Si-O stretching vibration. The spesific bands of organo montmorillonite which appeared at 2924 and 2854 cm–1 are corresponding to stretching asymmetric vibration ?as(CH2) and stretching symmetric ?s(CH2), respectively. The C-H stretch of CTA+ structure in-plane binding was noticed at 1473 cm–1. The bands at 516 and 462 cm–1 were assigned to the Al-O-Si (octahedral layer) bend for untreated and organo-montmorillonite, respectively. The BET specific surface area reduced with increasing surfactant concentrations. © 2018, Chemical Publishing Co. All rights reserved.
Group of Knowledge : Kimia
Original Language : English
Level : Internasional
Status :
Published
Document
No Title Document Type Action
1 Artikel dan Surat Keterangan Publikasi.pdf
Document Type : [PAK] Full Dokumen
[PAK] Full Dokumen View
2 Cek Similarity.pdf
Document Type : [PAK] Cek Similarity
[PAK] Cek Similarity View
3 Universitas Gadjah Mada Mail - Asian Journal of Chemistry (Galley Proof)-hilma.pdf
Document Type : [PAK] Bukti Korespondensi Penulis
[PAK] Bukti Korespondensi Penulis View