Title : Synthesis and characterization of Ni-promoted zirconia pillared bentonite
Author :

Mohamad Mirzan (1) Prof. Dr. rer. nat. Karna Wijaya, M.Eng. (2) Prof. Dr. Iip Izul Falah (3) Prof. Dra. Wega Trisunaryanti, M.S., Ph.D.,Eng. (4)

Date : 0 2019
Keyword : zirconia ,zirconia-pillared bentonite zirconia ,zirconia-pillared bentonite
Abstract : .The aim of this study was synthesis a catalyst applied to the cracking reaction and to characterize its physical-chemical properties. The catalyst is a zirconia-pillared bentonite with Nickel as a support metal (promotor). The catalyst is synthesized by pillarization bentonite with ZrOCl2•8H2O as a pillaring agent and then a calcination process for obtaining a zirconia pillared bentonit (ZrO2-bentonite). To obtain a catalyst with good cracking and hydrogenation activity, nickel metal (2% w/w) impregnation was performed using Ni(NO3)2•6H2O precursors. The next step is calcination and reduction to obtain a zirconia-pillared bentonite catalyst with Ni as a support metal (Ni/ZrO2-bentonite). To know the physical-chemical properties was characterized by XRF, XRD, acid properties test using ammonia absorption technique, FTIR and BET. The characterization results with XRF showed an increase of nickel metal content after impregnation process of 6.45%. The acidity assay with ammonia absorption technique showed an increase in the acid properties of the catalyst sample after pillarization and impregnation of 7.580 mmol/g. Analysis of sample diffraction patterns with XRD shows typical montmorillonite peaks still visible but shifts toward an angle of 2? ? 5°. Analysis of functional groups of catalyst with FTIR showed characteristic for Br?nsted acid at wave number 1635.64 cm-1 after impregnation with nickel metal. Surface area analysis results show an increase in specific surface area after pillarization and impregnation of 96.307 m2 /g.
Group of Knowledge : Kimia
Original Language : English
Level : Internasional
Status :
Published
Document
No Title Document Type Action
1 Mirzan_2019_J__Phys___Conf__Ser__1242_012013.pdf
Document Type : [PAK] Full Dokumen
[PAK] Full Dokumen View
2 mirzan_IOP_turnitin.pdf
Document Type : [PAK] Cek Similarity
[PAK] Cek Similarity View